High Strength and High Performance Concrete Materials and Difference

High Strength and High Performance Concrete Materials and Difference


High strength concrete and high-performance concrete are not synonymous because strength and performance of concrete are different properties of concrete. High-strength concrete is defined based on its compressive strength at a given age whereas high performance concrete is defined based on performance criteria namely: high durability, high strength, and high workability.

High-performance concrete is defined as a concrete that meets special combination of performance and uniformity requirements that cannot always be achieved routinely using conventional constituents and normal mixing, placing, and curing practice. However, high strength concrete is defined as concrete that has compressive strength of 55MPa or higher, as per ACI Code.

The use of high-performance concrete has overcome many problems observed in conventional concrete like less durability, weaker transition zone (aggregate-cement interface), low resistance to chemical attack and difficulty in repair and retrofitting works. High strength concrete has been used in the construction of many structures to decrease size of members, reduce dead load, and decline cost and construction materials.

Table 1 Difference between High Performance Concrete and High Strength Concrete

Items High Performance Concrete High Strength Concrete
Definition High-performance concrete is defined as concrete meeting special combinations of performance and uniformity requirements that cannot always be achieved routinely when using conventional constituents and normal mixing, placing and curing practices, as per ACI Code. High strength concrete is defined as concrete that has compressive of 55 MPa or greater.
Types    Chemical resistant concrete, early drying concrete, ultra-water resistant concrete, heat resistant concrete, and impact and abrasion resistant concrete. High Strength Concrete (50 – 100 MPa), ultra-High Strength Concrete (100 – 150 MPa), especial Concrete (> 150 MPa)
Strength criteria High strength, modulus of elastic, low creep and shrinkage It has high strength but does not necessarily possess superior characteristic as high-performance concrete
Durability criteria Resist scaling, freezing and thawing, chloride and carbonation, and prohibit bacterial and mold growth Durability of high strength is commonly improved by adding pozzolanic materials
Ductility Low ductility but can be improved by adding steel fibers It is brittle
Compositions Cement, fine aggregate, coarse aggregate, water, mineral admixtures; fine filler and/or pozzolanic supplementary cementation materials, chemical admixtures; plasticizers, superplasticizers, retarders, air-entraining agents) Cement, fine and coarse aggregate; fine aggregates with higher fineness modulus of around 3 is recommended, water, water reducing admixtures
Degree of quality control requirements It is sensitive to changes in constituent material properties, hence great degree of quality control is required for the successful production of high-performance concrete. High quality control is needed in order to maintain the special properties desired.
Production of concrete High performance concrete is produced by careful selection of raw materials such chemical admixtures and appropriate mix design to achieve the desired performance objectives.   High strength concrete is achieved at low water to cement ratio which is obtained by adding water reducing plasticizer or high range water reducing plasticizer. It is also essential to select a high-quality Portland cement, and optimize aggregates, then optimize the combination of materials by varying the proportions of cement, water, aggregates, and admixtures.
Placement and compaction Easy to pour and can be compacted without segregation. Placement would not be easy unless superplasticizer is used
Advantages For advantage of high-performance concrete please click here. Reduce maintenance and repair, decline size of members and cost of formworks, allow longer spans in bridge and hence decrease number of vertical supports, and permits construction of thinner slabs.
Disadvantages Need extensive quality control, costly, need special constituents, and need to be manufactured and placed careful. Low resistance to fire i.e. damage at high temperature, and need great expertise in selection of constituents.
Applications For applications of high-performance concrete please click here. High rise buildings, bridges with long spans, and high load carrying buildings built on weak soil.

Read More:

Requirements of High Performance Concrete

Normal Concrete vs. High-Strength Concrete Properties and Difference

Why do We Test Concrete Compressive Strength after 28 Days?

Applications of High-Performance Concrete in Civil Engineering

High-Performance Concrete: Composition, and Features

Mix Design of High Strength Concrete -Methods, Procedure and Example